Product Description This is a two component polyamide cured zinc rich epoxy coating. It is a high zinc dust containing product. It conforms to the compositional requirements of SSPC paint 20, level 2. It provides very good corrosion protection as part of a complete coating system. To be used as primer in atmospheric environments. Suitable for carbon steel, repair of inorganic zinc silicate coating and damaged galvanised steel substrates. This product complies with ASTM D520 type II zinc dust. Scope The Application Guide offers product details and recommended practices for the use of the product. The Application Guide (AG) must be read in conjunction with the relevant specification, Technical Data Sheet (TDS) and Safety Data Sheet (SDS) for all the products used as part of the coating system. Referred standards Reference is generally made to ISO Standards. When using standards from other regions it is recommended to reference only one corresponding standard for the substrate being treated. zinc epoxy Surface preparation and coating should normally be commenced only after all welding, degreasing, removal of sharp edges, weld spatter and treatment of welds is complete. It is important that all hot work is completed before coating commences. The required quality of surface preparation can vary depending on the area of use, expected durability and if applicable, project specification. Surface preparation Process sequence When preparing new surfaces, maintaining already coated surfaces or aged coatings it is necessary to remove all contamination that can interfere with coating adhesion, and prepare a sound substrate for the subsequent product. Inspect the surface for hydrocarbon and other contamination and if present, remove with an alkaline detergent. Agitate the surface to activate the cleaner and before it dries, wash the treated area using fresh water. Paint solvents (thinners) shall not be used for general degreasing or preparation of the surface for painting due to the risk of spreading dissolved hydrocarbon contamination. Paint thinners can be used to treat small localized areas of contamination such as marks from marker pens. Use clean, white cotton cloths that are turned and replaced often. Do not bundle used solvent saturated cloths. Place used cloths into water. When the surface is an existing coating, verify with technical data sheet and application guide of the involved products, both over coatability and the given maximum over coating interval. Soluble salts removal Soluble salts have a negative impact on the coating systems performance, especially when immersed. Jotun's general recommendations for maximum soluble salts (sampled and measured as per ISO 8502-6 and -9) content on a surface are: For areas exposed to (ISO 12944-2): C1-C4: 200 mg/m² C5M or C5I: 100 mg/m² read more

Product description This is a one component inert multipolymeric matrix coating. It is resistant to low temperatures, down to -196 °C and high temperatures, up to 650 °C continuously, 720 °C intermittent. Can be used as primer or finish coat in atmospheric environments. Suitable for properly prepared carbon steel and stainless steel substrates. It can be applied on hot substrates up to 400 °C. Protective: Specially designed for preventing corrosion under insulation (CUI). Recommended at dry operating surface temperatures that can range from cryogenic, i.e. -196 °C, to above 650 °C (intermittent 720 °C). Suitable for insulated and non insulated surfaces.  read more

Product description This is a two component isocyanate cured polyurethane coating. It is a high performance, non yellowing product. It is easy to apply. This product is tintable in a wide range of colours in Jotun's Multicolor Industry (MCI) system. It has excellent gloss and colour retention. It has good chemical, abrasion and impact resistance. If enhanced slip resistance is required Jotafloor Non Slip can be used in the system. To be used as topcoat in atmospheric environments. Suitable on approved primers on concrete substrates. Approvals and certificates Determination of Elongation - ASTM D2730 Determination of ease of decontamination - BS4247 Part 1:1987 Colours according to colour card and Multicolor Industry tinting system (MCI) Typical use Designed for a wide range of floors and walls with various levels of mechanical and chemical exposure. Specially designed for areas exposed to direct sunlight where gloss and colour stability is desired. Recommended as a topcoat as part of the car parks, parking bays, pedestrian walkways, industrial floors, drive ways, ramps and traffic deck systems. Additional certificates and approvals may be available on request. read more

Jotun Anti-Skid Product Description Jotun Anti-Skid is aluminium oxide grains, intended to be spread into the last coat in a non-skid system. Available in extra coarse, coarse, medium and fine particle sizes. Recommended Use For use on decks, floors, gangways and other areas where additional friction properties are required. The spreading is to take place in the wet film during application. Recommended Quantity Fine particle size (180 - 250 µm) for coatings applied in 50 to 150 µm DFT, such as topcoats. The recommended usage is 1,5 - 2,0 kg per 10 litres of paint Medium particle size (400 - 600 µm) for coatings applied in 150 to 400 µm DFT, such as Jotamastic products and thick film topcoats. The recommended usage is 2,5 - 3,3 kg per 10 litres of paint Coarse particle size (700 - 1000 µm) for coatings applied in 400 to 1500 µm DFT, such as Baltoflake products. The recommended usage is 3,0 - 4,0 kg per 10 litres of paint Extra Coarse particle size (1200 - 1600 µm) for coatings applied in 400 to 1500 µm DFT, such as Baltoflake products. The recommended usage is 3,5 - 4,0 kg per 10 litres of paint If a more rough surface is required, the quantity may be increased.   Physical Properties Colour Dark Solids (Vol %)* 100 ± Flash Point N.A. *Measured according to ISO 3233:1998 (E) Hong Kong rules: Category of paints - Other vessel coatings; Exempt compound - N/A; Specific gravity: 3.92 kg/ltr (Coarse); 3.92 kg/ltr (Fine); 3.92 kg/ltr (Medium); 3.92 kg/ltr (Extra Coarse). Both VOC and Specific gravity values provided are typical values, subject to changes when different colour involved. Surface Preparation Coated Surfaces According to specifications for the chosen topcoat. Other Surfaces The coating may be used on other substrates. Please contact your local Jotun office for more information. read more